We are using cookies to implement functions like login, shopping cart or language selection for this website. Furthermore we use Google Analytics to create anonymized statistical reports of the usage which creates Cookies too. You will find more information in our privacy policy.
OK, I agree I do not want Google Analytics-Cookies
International Journal of Periodontics & Restorative Dentistry



Forgotten password?


Dear readers,

our online journals are moving. The new (and old) issues of all journals can be found at
In most cases you can log in there directly with your e-mail address and your current password. Otherwise we ask you to register again. Thank you very much.

Your Quintessence Publishing House
Int J Periodontics Restorative Dent 39 (2019), No. 2     25. Mar. 2019
Int J Periodontics Restorative Dent 39 (2019), No. 2  (25.03.2019)

Page 213-218, doi:10.11607/prd.3998, PubMed:30794257

Capacity to Maintain Placement Torque at Removal, Single Load-to-Failure, and Stress Concentration of Straight and Angled Abutments
Sousa, Michelle Paulino / Tribst, João Paulo Mendes / de Oliveira Dal Piva, Amanda Maria / Borges, Alexandre Luiz Souto / de Oliveira, Sérgio / da Cruz, Paulo César
Because the main complication of implant-supported prostheses is torque loosening and/or fixation screw fracture, the goal of this study was to evaluate the torque before and after fatigue (screw placement and removal, respectively), single load-to-failure (compression test), and stress concentration of straight and angled abutments. Eighty implants were included in polyurethane cylinders. Half of the implants received straight abutments (group S, n = 40) and the other half received angled abutments (group A, n = 40). The abutments for cemented prostheses were installed with a torque of 20 Ncm. Eighty titanium structures were machined and cemented on the abutments with zinc-phosphate cement. After storage for 24 hours, half of the specimens had their torque loosening evaluated and were then immediately submitted to a compressive test in a universal testing machine (1 mm/minute, 1,000 kgf), while the other half were subjected to cyclic fatigue (200 N at 2 Hz for 2 × 106 cycles at 37°C) as an aging protocol (n = 20 from each group). The aged samples then had their torque loosening measured and were also submitted to the compression test. Representative samples were evaluated by scanning electron microscopy. Two bidimensional models similar to the in vitro specimens were created and analyzed using the finite element method to evaluate the stress concentration. Data from the in vitro tests were submitted to two-way analysis of variance and Tukey test, both with significance at P = .5. The results show that angled abutments are less capable of maintaining the installation torque and are less resistant during the single load-to-failure test. The von Mises stress concentration was higher for group A in the cervical region. The straight abutments have better prognosis than angled abutments and less susceptibility to mechanical failures.